Williams 150 KSI Fully Threaded Bar Introduction
Williams 1” through 1-3/8” 150 KSI bars are smooth, hot rolled, high strength prestressing steel. The bars are cold-stressed and stress relieved in strict compliance with ASTM A722 and AASHTO M275 Highway Specifications. The 1-3/4” through 3” 150 KSI bars are made from alloy steel that is hot rolled, quenched and tempered to meet to the prescribed mechanical properties of ASTM A722.
| NOMINAL BAR DIAMETER & PITCH | MINIMUM NET AREA THRU THREADS | MINIMUM ULTIMATE STRENGTH | PRESTRESSING FORCE | NOMINAL WEIGHT | APPROX. THREAD MAJOR DIA. | PART NUMBER | ||
|---|---|---|---|---|---|---|---|---|
| 0.80F PU A | 0.70F PU A | 0.60F PU A | ||||||
| 1” – 4 (26 mm) | 0.85 in2 (549 mm2) | 128 kips (567 kN) | 102 kips (454 kN) | 89.3 kips (397 kN) | 76.5 kips (340 kN) | 3.09 lbs/ft (4.6 kg/m) | 1-1/8” (29 mm) | R71-08 |
| 1-1/4” – 4 (32 mm) | 1.25 in2 (807 mm2) | 188 kips (834 kN) | 150 kips (667 kN) | 131 kips (584 kN) | 113 kips (500 kN) | 4.51 lbs/ft (6.7 kg/m) | 1-7/16” (37 mm) | R71-10 |
| 1-3/8” – 4 (36 mm) | 1.58 in2 (1019 mm2) | 237 kips (1054 kN) | 190 kips (843 kN) | 166 kips (738 kN) | 142 kips (633 kN) | 5.71 lbs/ft (8.5 kg/m) | 1-9/16” (40 mm) | R71-11 |
| 1-3/4” – 3-1/2 (46 mm) | 2.60 in2 (1664 mm2) | 390 kips (1734 kN) | 312 kips (1388 kN) | 273 kips (1214 kN) | 234 kips (1041 kN) | 9.06 lbs/ft (13.5 kg/m) | 2” (51 mm) | R71-14 |
| 2-1/4” – 3-1/2 (57 mm) * | 4.08 in2 (2632 mm2) | 613 kips (2727 kN) | 490 kips (2181 kN) | 429 kips (1909 kN) | 368 kips (1636 kN) | 14.1 lbs/ft (20.8 kg/m) | 2-1/2” (64 mm) | R71-18 |
| 2-1/2” – 3 (65 mm) | 5.19 in2 (3350 mm2) | 778 kips (3457 kN) | 622 kips (2766 kN) | 545 kips (2422 kN) | 467 kips (2074 kN) | 18.2 lbs/ft (27.1 kg/m) | 2-3/4” (70 mm) | R71-20 |
| 3” – 3 (75 mm) | 6.85 in2 (4419 mm2) | 1027 kips (4568 kN) | 822 kips (3656 kN) | 719 kips (3198 kN) | 616 kips (2740 kN) | 24.1 lbs/ft (35.8 kg/m) | 3-1/8” (80 mm) | R71-24 |
Williams 150 ksi All Thread Bar
Williams all thread bar of 150 ksi has been widely used in many industrial applications which requires high tensile and yield strength. With the right material, heat treatment would make the steel rod exceed post tensioning bar and rock anchoring conditions, and after it passed 500,000 times of loading, it makes a very suitable fastener to help create large bond strength to grout or concrete.
- AASHTO M275
This specification covers Type I and Type II high-strength steel bars intended for use in prestressed concrete construction or in prestressed ground anchors. Bars are of a minimum ultimate tensile strength level of 1035 MPa [150,000 psi]. - ASTM A722
This specification covers Type I and Type II high-strength steel bars intended for use in prestressed concrete construction or in prestressed ground anchors. Type I bars have a plain surface. Type II bars have surface deformations. Bars are of a minimum tensile strength level of 150 000 psi [1035 MPa].
Mechanical Property of 150 Ksi All Thread Rod
| YIELD STRESS | ULTIMATE STRESS | ELONGATION IN 20 BAR DIAMETERS | REDUCTION OF AREA |
|---|---|---|---|
| 120 KSI (827 MPa) | 150 KSI (1034 MPa) | 4% | 20% min. |
Longteng 150 Ksi All Thread Rod
AGICO is a high strength steel product supplier in China, we mainly supplies high tensile strength steel rod and bar products such as anchor rod, stud bolt, hexagonal bolt etc. AGICO has developed equivalent fully threaded bar according to the famous William 150 ksi bar, usually our 150 ksi all thread rod tensile strength exceed the standard value of 1026 Mpa. Our all thread bar and bolt products have super high yield strength(up to 1100 MPa) and tensile strength(up tp 1220 MPa). Regarding impact energy, our grade 8.8 anchor bolt everages 60J , grade 10.9 everages 35J which means our products performance much higher than standard requirements.
Lonteng 150 Ksi Fully Threaded Bar Sample Order
| Manufacturer | Anyang AGICO | Product | Pre-stress Anchor | Customer | x | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Address | Industrial Park, Indu District, | Standard | Acc. to Agreement | Grade | 42CrMoA | Dimension(mm) ： M39 Specification | ||||||||
| Tel/Fax | 0372-2256666 | Delivery | 2022/2/22 | (D Weight | 10.803 | Qty: 5 | ||||||||
| Delivery Condition | Manufacture certificate No. | |||||||||||||
| Turbine No. | Production No. | Length (mm) | Qty (pcs) | Weight (T) | Mechanical Property | Magnetic Test(100%) | Corrosion Protection | Cross section area (mm2) | Appearance | |||||
| Non-proportional extension strength ReH (MPa) | Yield Strength Rm(MPa) | Elongation(%) | Rate of reduction% | -40V Impact Energy (J) | Hardness HV | |||||||||
| LT10.9 M39-01 | 5220210002 | 3745 | 176 | 5.356 | 1002 | 1096 | 14.5 | 50 | 41 | 363 | Qualified | Qualified | / | Qualified |
| LT10.9 M39-02 | 5220210001 | 3745 | 176 | 5. 356 | 1017 | 1118 | 15.5 | 50 | 48 | 363 | ||||
| LT10.9 M39-B01 | 5220210004 | 3745 | 3 | 0.091 | 1028 | 1122 | 16.0 | 51 | 54 | 349 | ||||
AGICO supplies equivalent standard of Williams 150 Ksi All Threaded Bar Product, and our fully threaded bar can exceed the basic requirement of 1026 Mpa, if you are interested in finding out the difference between 150 Ksi William full thread bar and AGICO All Thread Rod, send a message now for more details.